Dye-sensitized solar cell based on nanocrystalline TiO<Subscript>2</Subscript> with 3–10 nm in diameter

Nanocrystalline TiO₂ with 3–10 nm in diameter was prepared with a surfactant-template method. Dye-sensitized solar cells were assembled using the prepared nanocrystalline TiO₂ with large surface area and high crystallinity, which achieved significant higher Jsc when compared to cells fabricated with bigger particles of 25 nm in diameter. In the cells with nanocrystalline TiO₂, the sintering temperature drastically affected the conversion performance of the cells.     

Dielectric behavior of Cu–GeO<Subscript>2</Subscript> cermet thin films

Capacitance and dielectric loss measurements were carried out using an Al/Cu–GeO₂/Al sandwich structure for 0 to 10 vol% Cu films, 120–400 nm thick, deposited at 0.4–1.5 nm/s in the frequency and temperature range 1–10⁶ Hz and 90–573 K, respectively. The variation of capacitance and dielectric loss with frequency and temperature follows the Goswami and Goswami model. Capacitance decreases slowly with increasing thickness and also varies with the change in deposition rate of the cermet film.     

Efficient and stable field emission from the oxidized porous polysilicon using Pt/Ti multilayer electrode

The field emission characteristics of an oxidized porous polysilicon (OPPS) were investigated with a Pt/Ti multilayer electrode, which showed highly efficient and stable electron emission characteristics compared with those of conventional Au/NiCr electrodes. The thin Ti layer played an important role in promoting the adhesion of Pt to SiO₂ surface and the distribution of the electric field on the OPPS surface. Additionally, the Ti layer efficiently blocked the diffusion of emitter metal, which resulted in more reliable emission characteristics.     

Identification of microstructural zones and thermal cycles in a weldment of modified 9Cr-1Mo steel

This paper presents the results of a study on the microstructural and microchemical variations in a multipass Gas Tungsten Arc weld (GTAW) of modified 9Cr-1Mo steel. The changes brought about in the steel due to the heating and cooling cycles during welding and the subsequent effects due to reheating effects during multipass welding are described. Detailed analytical transmission electron microscopy has been carried to study the type and composition of the primary and secondary phases in this steel. The systematic changes in microstructural parameters such as Prior Austenite Grain Size, martensite lath size, number density, size and microchemistry of carbides, have been understood based on the different transformations that the steel undergoes during the heating and cooling process. Based on the observed microstructure, an attempt has been made to identify distinct microstructural zones and possible thermal cycles experienced by different regions of the weldment.     

Effect of preparation technique on the properties of Mo-containing Al-MCM-41

The Al-MCM-41 has been used as support to prepare Mo-containing catalysts. The 12- molybdophosphoric heteropoly acid (HPMo) is used as initial compound. The catalysts are synthesized by two different methods: incipient impregnation with aqueous solution of the acid and mechanochemical synthesis. The samples were tested in the reaction of the thiophene hydrodesulfurization after activation with mixture H₂ + H₂S. The effect of the preparation method of the catalysts on their physicochemical and catalytic properties has been studied. A partial destruction of the loaded compound is observed in mechanochemically treated sample whereas the aggregates are formed from the particles of different size in the impregnated sample. The specific surface area of the sample prepared by mechanical–chemical treatment decreases 2–3 times, while the total pore volume is about four times lower. The HDS activity is higher on the impregnated sample than on the mechanochemically treated one.     

Improved visible-light responsive photocatalytic activity of N and Si co-doped titanias

Thermal reaction of titanium tetraisopropoxide and tetraethyl orthosilicate in 1,4-butanediol afforded nanocrystalline silica-modified titanias having large surface area and superior thermal stability. In this study, the thus-obtained silica-modified titanias were treated in an NH₃ flow at high temperatures, and their physical and photocatalytic properties were investigated. Compared with NH₃-treated TiO₂ without silica modification, the NH₃-treated silica-modified titanias showed a stronger absorption in the visible region (400–500 nm) and had a larger peak at 396 eV in the N 1s XPS spectrum. These results indicate that a larger amount of nitrogen was stably doped in the silica-modified titania. The obtained products exhibited a high photocatalytic activity for degradation of Rhodamine B and decomposition of acetaldehyde under visible light irradiation. Electronic supplementary material The online version of this article (doi:) contains supplementary material, which is available to authorized users.     

Optimized hydrogen positions for aluminium and iron containing hydroxide minerals

The structures of a number of hydroxide and oxyhydroxide minerals have previously been reported without the hydrogen positions explicitly defined. Here we use two atomic scale computer simulation techniques, one based on classical ionic potentials, the other on density functional theory (DFT), to predict these positions. The aim is not only to provide data that can be used as the basis for future experimental structure optimizations but also model parameters that can be used to predict complex hydroxide structures. The efficacy of the approach is demonstrated through the comparison of predicted and experimental data for minerals whose hydrogen positions are known.     

Electrical characterization of carbon nanotube Y-junctions: a foundation for new nanoelectronics

A review on the syntheses and electrical characterization of Y-shaped multi-walled carbon nanotube morphologies is presented. Modified thermal CVD processes, using Ti precursors, are used to grow Y-junctions of different geometries and distribution of catalyst particles. It has been established that novel electrical switching behavior is feasible, where any one of the three branches of the Y-junction can be used for modulating the electrical current flow through the other two branches. Current blocking behavior, leading to perfect rectification, is seen which could be related to the interplay of the carrier lifetime and the transit time. The overall goal is to investigate the possibility of obtaining novel functionality at the nanoscale, which can lead to new device paradigms.     

On the non-destructive detection of fatigue damage in industrial aluminium alloys by positron annihilation

The average positron lifetime has been determined non-destructively and in-situ during fully symmetric push-pull fatigue experiments in the bulk material of the aluminium alloys 2024 T3 and 7075 T6 using a servo-hydraulic fatigue testing system equipped with a mobile positron beam produced by a ⁷²Se/⁷²As generator (initial activity of ≈ 0.9 MBq; average positron penetration depth ≥1 mm). Contrary to earlier investigations on stainless steel using the same experimental approach, no variation of the average positron lifetime could be observed during fatigue and neither early nor late stages of fatigue damage could be revealed. It is concluded that fatigue induced changes of the defect spectra in technologically relevant aluminium alloys are masked for the present method by saturation trapping in precipitates. A sufficiently high increase of the dislocation density and the creation of vacancy clusters must be confined to the vicinity of propagating fatigue cracks or the fatal fatigue crack. Therefore the zone with sufficient detectable fatigue damage has not enough statistical weight to modify the average positron lifetime of the aluminium alloy bulk material.     

Critical slowing down in lead magnesium niobate–zirconate ceramic

Dielectric relaxation behaviour of (1 − x)PMN − xPZ, for x = 0.10, 0.30 and 0.40 have been studied. The nature of relaxational behaviour was found to change with PZ concentration. A crossover from a static freezing to critical slowing down like behaviour is observed with increase in Zr⁴⁺ concentration. We have used Glazounov and Tangastev criterion to distinguish freezing and critical slowing down like behaviour.